Surface protection

In accordance with DBL 9440.40 (silver-coloured zinc flake coating with lubrication integrated in seal, Cr(VI)-free) > VDA 235 – 104.42

Corrosion resistance

≤ M8 - approx. 480 hrs, no base metal corrosion acc. to DIN EN ISO 9227 – NSS
≥ M10 - approx. 720 hrs, no base metal corrosion acc. to DIN EN ISO 9227 – NSS
The specified corrosion resistances apply for the corrosion tests according to DIN EN ISO 9227-NSS (salt spray mist testing), at the earliest 24 h after coating in the "as coated" state, i.e. before sorting, packaging, transporting and/or assembly. These values can be reduced through inevitable handling and assembly processes.

A transfer of the corrosion resistances from the salt spray mist test to real assembly and operating conditions is not possible in the majority of cases. When designing a connection both the combined materials and if necessary coatings as well as the environmental conditions during operation must be considered by the designer in the selection of a suitable corrosion protection coating.

Friction coefficient

μ tot = 0.09 – 0.14 (VDA 235 – 101)

Notice
Flange head screws reduce the risk of pretension loss caused by setting of contact surfaces. The surface pressure generated under the screw head during tightening is low compared to conventional hexagon heads (without flange), as the force is distributed over a larger contact surface.

Advantage:

Less setting required due to fewer parts to be connected compared to connections using washers.
The concave washer pressing against the contact surface increases the elasticity of the connection so that the setting/creeping movements that occur are counteracted and pretension loss is generally prevented
Matching nuts

Hexagon nut with flange and clamping piece MBN 13032 Steel 10, zinc flake coating,